Weartuf400 Abrasion Resistant Plate Drilling Weartuf500 Steel Mirror Sheet 1m 1.5m

Place of Origin Mainland China
Brand Name Hengchengtai
Certification SGS ISO ROHS
Model Number WEARTUF400 450 500
Minimum Order Quantity 1ton
Price 500-1000 USD PER TON
Packaging Details standard waterproof package
Delivery Time 5-10Days after confirming order
Payment Terms L/C, T/T, Western Union
Supply Ability 800TONS PER MONTH
Product Details
Hardness 300-500HBV Width 1m 1.25m 1.5m 1.8m 2.2m 2.5m As Customized
Length 1m 1.5m 2.4m 3m 5.8m 12m As Customized Thickness 1.0-150mm
Processing Service Bending Cutting Welding Punching Trading Term CIF CFR FOB EXW
Yield Strength 1000mpa Tensile Strength 1100mpa
Ultimate Strength 1000mpa Elongation 40%
Testing Third Party Inspection Available Surface Mill Surface
High Light

Weartuf400 abrasion resistant plate

,

abrasion resistant plate Drilling Weartuf500

,

steel mirror sheet 1m 1.5m

Leave a Message
Product Description

Weartuf400 is a Singapore wear-resistant plate. Wuxi weartuf400 corresponds to the national standard nm400. The typical Brinell hardness is 400hbw. The high impact toughness of weartuf400 gives the steel plate good crack resistance in the process of manufacturing and use.


Chemical compoition

Steel Grade
C
Si
Mn
P
S
Cr
Mo
Ni
Ti
NM300/AR300/WearTuf300
0.23
0.70
1.60
0.025
0.015
0.70
0.40
0.50
0.050
NM360/AR360/WearTuf360
0.25
0.70
1.60
0.025
0.015

 

0.80
0.50
0.50
0.050
NM400/AR400/WearTuf400
0.30
0.70
1.60
0.025
0.010
1.00
0.50
0.70
0.050
NM450/AR450/WearTuf450
0.35
0.70
1.70
0.025
0.010
1.10
0.55
0.80
0.050
NM500/AR500/WearTuf500
0.38
0.70
1.70
0.020
0.010
1.20
0.65
1.00
0.050
NM550/AR550/WearTuf550
0.38
0.70
1.70
0.020
0.010
1.20
0.70
1.00
0.050
NM600/AR600/WearTuf600
0.38
0.70
1.90
0.020
0.010
1.50
0.70
1.00
0.050
Machinery property
Steel Grade
Tensile/Mpa
Elongation/%
Hardness/HBW
-20ºC Impact energy Akv/J
NM300/AR300/WearTuf300
>1000
>14
270-330
>24
NM360/AR360/WearTuf360
>1100
>12
330-390
>24
NM400/AR400/WearTuf400
>1200
>10
370-430
>24
NM450/AR450/WearTuf450
>1250
>7
420-480
>24
NM500/AR500/WearTuf500
-
-
480-525
>24
NM550/AR550/WearTuf550
-
-
>530
-
NM600/AR600/WearTuf600
-
-
>570
-

Weartuf400 technical standard: eniso148-1

Weartuf400 wear plate delivery status: quenched (q) tempered (T)

Imported Singapore wear-resistant board weartuf400 is cut for retail, and the spot thickness is 6-50mm. Preheating is always required when cutting steel plates from imported wear-resistant plates. It is recommended that the forming temperature be between 150-200 ºC. Preheating will improve the deformation of the steel plate and ensure the success of bending. Worn things, lack of smoothness, defects in the appearance of steel plate and burrs at the cutting edge will affect the forming quality. It is recommended to use the allowable * bending radius. The steel plate shall be bent to curvature in a single pass to prevent rebound during operation. The smooth appearance of twists and turns will reduce friction. The basic requirement for successful bending and bending is that the steel plate stored in the cooling environment should be thoroughly preheated to room temperature + 20 ºC before starting the operation. All quenched steel plates and sheets must be formed with special care.

Weartuf500 wear plate hardness, average 500hbw, Brinell hardness. The microstructure of this wear-resistant steel is martensitic structure, which can ensure the high hardness and tensile hardness of the steel plate. The hardness of weartuf400 is 2.5 times that of S355 structural steel. The high hardness and tensile strength make the imported Singapore wear-resistant plate weartuf 400 have high wear resistance in rolling contact. Despite its high hardness and strength, weartuf400 can be formed by free bending or crimping, and has good weldability. Because it can withstand the wear of rolling contact and high surface pressure, the hardened steel can be used to greatly reduce the cost caused by the wear and loss of structural components.

Wearuf 400 wear plate dimensions

Weartuf400 is available in the thickness range of 6.0-50.0mm. Depending on the thickness of the steel plate, the width can reach 3100mm and the length can reach 18000mm.

Weartuf500 wear plate hardness: 470-510hbw

According to the standard EN ISO 6506-1, the surface Brinell hardness shall be tested after the steel plate surface is milled to a depth of 0.5-2.0mm.

Small center hardness:

Steel plate thickness ≤ 20mm: surface hardness * small guarantee value, 370hbw

Steel plate thickness > 20mm: surface hardness * 95% of small guarantee value

Main uses of weartuf400: it is widely used in crusher, crusher, dump truck carriage, container, sieve plate, feeder, feeding funnel, elevator, blade plate, conveyor, bucket, knife plate, gear, sprocket, lining plate, bolt fixed blade, wear strip, chute, cutter, hammer, etc